Kimya PETG Carbon Black | 2.85mm | 2.2kg

Sale

Original price was: £231.97.Current price is: £220.37. (excl. VAT)

The Kimya PETG Carbon 3D filament is a mixture of PETG and carbon fibres. The addition of carbon fibres to PETG provides high levels of mechanical performance.

Please scroll down to see full product details 👇

Product details

Thanks to its rigidity, the PETG Carbon is highly valued in the production of special parts, notably in the paramedical and automotive fields. The Kimya PETG Carbon 3D filament has the following properties:

High rigidity
Improve ratio between: Ease of printing / Rigidity
Complies with the REACH standard

Print Parameters and Specimens Dimensions

PRINTING DIRECTION	XY
Printing Speed	40-70 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	220-260°C
Bed T°	60-100°C

Filament Properties

PROPERTIES	TEST METHODS	VALUES
Density	ISO 1183-1	1.28 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@225°C – 2.16 kg)	9.7 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-300°C)	76 °C

Printed Specimens Properties

PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	4,541 MPa
	Tensile Strength	ISO 527-2/5A/50	52.9 MPa
	Tensile strain at strength	ISO 527-2/5A/50	2.4 %
	Tensile Stress at Break	ISO 527-2/5A/50	41.3 MPa
	Tensile strain at break	ISO 527-2/5A/50	2.6 %
	Flexural modulus	ISO 178	2,648 MPa
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	80.4 MPa
	Flexural stress at break	ISO 178	80 MPa
	Charpy impact resistance	ISO 179-1/1eA	4.1 kJ/m²
	Shore Hardness	ISO 868	75D

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values – Properties can be influenced by production conditions.