The Kimya PEKK-SC 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a semi-crystalline thermoplastic polymer. PEKK-SC is PEKK in semi-crystalline form, imparting it with increased heat resistance. It is therefore resistant to high temperatures, abrasion and chemical products. Manufactured from KEPSTAN® Arkema, PEKK has excellent mechanical properties. Manufacturers use it to produce components exposed to acids and hydrocarbons, such as fuel and lubricants. It is compatible with the smoke/fire standard EN 45 545 – essential in the railway sector. The Kimya PEKK-SC 3D filament has the following properties:

Semi-crystalline structure
Excellent mechanical properties
Heat resistance (up to 260°C)
Railway fire and smoke standard EN45545
Aerospace FAR 25.853 Standard
Flame retardant – eligible to UL94 V0
Complies with the RoHS and REACH standard
Product Dimensions: 20.7 × 20.5 × 6 cm; 0.55 kg

FILAMENT PROPERTIES

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.27 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@380°C – 5 kg)	35 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-410°C)	161 °C
Heat distortion temperature (HDT) (1.8 MPa)	ISO 75f	172°C
Melting Temperature (Tm)	ISO 11357-1 DSC (10°C/min – 20-410°C)	332 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION	XZ	ZX
Infill Angle	45°/-45°	45°/-45°

PRINTED SPECIMENS PROPERTIES

	PROPERTIES	TEST METHODS	XZ	ZX
ELECTRICAL PROPERTIES	Dielectric strength	IEC 60243-1 (100µm)	84 kV/mm	84 KV/mm
	Relative permittivity	IEC 60250 (1 MHz)	2.6	2.6
	Loss tangent	IEC 60250 (1 kHz)	0.007	0.007
	Surface resistivity	ASTM D257	10¹⁶ Ohms/m²	10¹⁶ Ohms/m²
	Volume resistivity	ASTM D257	10¹⁶ Ohms/cm	10¹⁶ Ohms/cm
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/1A/50	2,448 MPa	2,784 MPa
	Tensile Strength	ISO 527-2/1A/50	64.1 MPa	32.4 MPa
	Tensile strain at strength	ISO 527-2/1A/50	4.5 %	1.4 %
	Tensile Stress at Break	ISO 527-2/1A/50	64.1 MPa	32.4 MPa
	Tensile strain at break	ISO 527-2/1A/50	4.5 %	1.4 %
	Flexural modulus	ISO 178	1,918 MPa	1,705 MPa
	Flexural strength*	ISO 178		62.9 %
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	79.3 MPa	61.6 MPa
	Flexural stress at break	ISO 178		62.9 MPa
	Flexural strain at flexural strength	ISO 178		3.8 %
	Charpy impact resistance	ISO 179-1/1eA	5.35 kJ/m²	1.9 kJ/m²

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values – Properties can be influenced by production conditions.