Fiberthree F3 PA-CF Lite Black | 2.85mm | 2kg

Sale

Original price was: £322.48.Current price is: £306.36. (excl. VAT)

Technical filament from polyamide modified for 3D-printing in FFF with additional carbon fibers.

Please scroll down to see full product details 👇

Original price was: £322.48.Current price is: £306.36. (excl. VAT)

Buy Now

Add to cart

Product details

Technical filament from polyamide modified for 3D-printing in FFF with additional carbon fibers.

The carbon fibers reduce the shrinkage and the warping behaviour extremely. Material shows excellent strength with remaining impact resistance.
Recommended for all parts with good heat- and media resistance where light weight or high strength matters.
Printed parts show an excellent matte surface finish.
The material differs in the print process from F3 PA-CF Pro in reduced moisture sensitivity and need for much more heat intake in the hotend for proper layer adhesion.
The stiffness of the filament should be considered for the pipes and the feeder system of the printer to avoid breaking.

Density	g/ cm³	1,24
Modulus of Elasticity printed specimen	MPa (N/mm²)	11500
Tensile strength printed specimen x-y (+ 45°/-45°)	MPa (N/mm²)	65
Tensile strength printed specimen x-y (0°)	MPa (N/mm²)	90
Tensile strength printed specimen x-y (90°)	MPa (N/mm²)	30
Tensile stress printed specimen x-y (0°)	MPa (N/mm²)	—
Elongation printed specimen (0°)	%	—
Flexural modulus printed specimen (+ 45°/-45°)	GPa (kN/mm²)	4,12
Impact strength printed specimen x-y (+ 45°/-45°)(Charpy)	kJ/m²	35
Shore hardness	—	—

Glass transition temp.	°C	87
Heat distortion temp.(HDT)	°C	90