Sale

Kimya PLA-HI Orange | 2.85mm | 750g

Sale

Original price was: £40.41.Current price is: £38.39. (excl. VAT)

The Kimya PLA-HI 3D filament is a biosourced polymer obtained from corn starch. Polylactic Acid -HI (PLA-HI) is a high Impact filament offering increased impact resistance.

Please scroll down to see full product details 👇

Product details

The Kimya PLA-HI 3D filament is a biosourced polymer obtained from corn starch. Polylactic Acid -HI (PLA-HI) is a high Impact filament offering increased impact resistance. It was formulated to be four times more resistant to impact than standard PLA. PLA is easy to print and odorless. It can be used to create functional prototypes, spare parts, architectural models, and in other forms of modeling. The Kimya PLA-HI 3D filament has the following properties:

Easy to print
Impact resistance
Odorless
Biosourced material
Food contact under EU10/2011
Complies with the REACH standard

FILAMENT PROPERTIES

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.21 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@210°C“ 2,16 kg)	5.7 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-220°C)	60 °C
Melting Temperature (Tm)	ISO 11357-1 DSC (10°C/min“ 20-220°C)	156 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION	XY
Printing Speed	40-150 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	190-210°C
Bed T°	20-60°C

PRINTED SPECIMENS PROPERTIES

	PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES
	Tensile modulus	ISO 527-2/5A/50	2,491 MPa
	Tensile Strength	ISO 527-2/5A/50	43 MPa
	Tensile strain at strength	ISO 527-2/5A/50	2 %
	Tensile Stress at Break	ISO 527-2/5A/50	22.9 MPa
	Tensile strain at break	ISO 527-2/5A/50	4.2 %
	Flexural modulus	ISO 178	2,097 MPa
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	62.8 MPa
	Charpy impact resistance	ISO 179-1/1eA	16.5 kJ/m²
	Shore Hardness	ISO 868	76,8D

Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.

Note 2 The data should be considered as indicative values – Properties can be influenced by production conditions.

Print Setting

Print speed: 40-150 mm/s
Extrusion temperature: 190-210°C
Platform temperature: 20-60°C

Miscellaneous

Highlight	Easy To Print
Highlight 2	Shiny Appearance
Highlight 3	Bright Colors
Highlight 4	Biosourced
Spool Material	PC
Steaming Temperature	80°C
Steaming Duration	2h-4h