Kimya PA6-CO Black 1.75mm 4.5kg

Sale

Original price was: £467.53.Current price is: £444.15. (excl. VAT)

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior.

Please scroll down to see full product details 👇

Original price was: £467.53.Current price is: £444.15. (excl. VAT)

Buy Now

Add to cart

Product details

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior. Unlike other polyamide filaments on the market the PA6-CO is very easy to print and can be used seamlessly on open chamber 3D printers. It is the perfect standard polyamide go-to thanks to its inherent polyamide properties of high mechanical, chemical and heat resistance. Due to the general moisture sensitivity of polyamides, the filament must be dried before printing.

Excellent printability even on open chamber printers
Low warping
Good wear resistance

2-years KIMYA warranty.
Store away from light, humidity and heat to maintain the properties of the product.

Filament Properties

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	2.85 ± 0.1 mm
Density	ISO 1183-1	1.157 g/cm3
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-300°C)	65 °C
Melting Temperature (Tm)	ISO 11357-1 DSC (10°C/min – 0-300°C)	227 °C

Print Parameters and Specimens Dimensions

PRINTING DIRECTION	XY
Printing Speed	55 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	270°C
Bed T°	75°C

Printed Specimens Properties

	PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	2,166 MPa
	Tensile Strength	ISO 527-2/5A/50	56.1 MPa
	Tensile strain at strength	ISO 527-2/5A/50	4.3 %
	Tensile Stress at Break	ISO 527-2/5A/50	13.4 MPa
	Tensile strain at break (type A)	ISO 527-2/5A/50	<14 %
	Flexural modulus	ISO 178	2,017 MPa
	Deformation at Flexural Strain	ISO 178	<5 %
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	65.9 MPa
	Charpy impact resistance	ISO 179-1/1eA	3.9 kJ/m²
	Shore Hardness	ISO 868	77,3

Once the spool is dried, we recommend that it be used within 24 hours and maximum 7 days without drying.

We have carried out several printing tests on Kimya PA6-CO and recommend the following:

Extrusion temperature: 260 – 290°C
Plate temperature: 75 – 100C
Printing speed: 40 – 70 mm/s

3D Printing Profiles

3D Printer	Last update
Ultimaker S3	07/07/2022
Ultimaker S5	07/07/2022

PROPERTIES	RATING
Ease to print	4/5
Rigidity	4/5
Impact Strength	2/5
Sensitivity to moisture	4/5
Temperature resistance	2/5
Weather Resistance	3/5
RoHs	Compliant
EU 10/2011	Non Compliant
FDA	Non Compliant
UL94 – V0	Non Compliant
ESD Protection	Non Compliant