Kimya PA6-CO Black 2.85mm 750g

Sale

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior.

Please scroll down to see full product details 👇

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Buy Now
Add to cart

Product details

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior. Unlike other polyamide filaments on the market the PA6-CO is very easy to print and can be used seamlessly on open chamber 3D printers. It is the perfect standard polyamide go-to thanks to its inherent polyamide properties of high mechanical, chemical and  heat resistance. Due to the general moisture sensitivity of polyamides, the filament must be dried before printing.

  • Excellent printability even on open chamber printers
  • Low warping
  • Good wear resistance

2-years KIMYA warranty.
Store away from light, humidity and heat to maintain the properties of the product.

Filament Properties

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 2.85 ± 0.1 mm
Density ISO 1183-1 1.157 g/cm3
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min – 20-300°C) 65 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 0-300°C) 227 °C

Print Parameters and Specimens Dimensions

PRINTING DIRECTION XY
Printing Speed 55 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 270°C
Bed T° 75°C

Printed Specimens Properties

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,166 MPa
Tensile Strength ISO 527-2/5A/50 56.1 MPa
Tensile strain at strength ISO 527-2/5A/50 4.3 %
Tensile Stress at Break ISO 527-2/5A/50 13.4 MPa
Tensile strain at break (type A) ISO 527-2/5A/50 <14 %
Flexural modulus ISO 178 2,017 MPa
Deformation at Flexural Strain ISO 178 <5 %
Flexural stress at conventional deflection (3,5% strain)* ISO 178 65.9 MPa
Charpy impact resistance ISO 179-1/1eA 3.9 kJ/m²
Shore Hardness ISO 868 77,3

Once the spool is dried, we recommend that it be used within 24 hours and maximum 7 days without drying.

We have carried out several printing tests on Kimya PA6-CO and recommend the following:

Extrusion temperature: 260 – 290°C
Plate temperature: 75 – 100C
Printing speed: 40 – 70 mm/s

3D Printing Profiles

3D Printer Last update
Ultimaker S3 07/07/2022
Ultimaker S5 07/07/2022
PROPERTIES RATING
Ease to print 4/5
Rigidity 4/5
Impact Strength 2/5
Sensitivity to moisture 4/5
Temperature resistance 2/5
Weather Resistance 3/5
RoHs Compliant
EU 10/2011 Non Compliant
FDA Non Compliant
UL94 – V0 Non Compliant
ESD Protection Non Compliant

Sale

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Need help? info@dream3d.co.uk / 02070888163

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Buy Now
Add to cart

or

Buying in bulk or multiple items?

Ongoing Tech Support

Thousands of products available for next day delivery

You might also like

Select the fields to be shown. Others will be hidden. Drag and drop to rearrange the order.
  • Image
  • SKU
  • Rating
  • Price
  • Stock
  • Availability
  • Add to cart
  • Description
  • Content
  • Weight
  • Dimensions
  • Additional information
Click outside to hide the comparison bar
Compare

Contact us for a quote