Kimya PC-S Translucent 2.85mm 750g

Sale

Original price was: £42.50.Current price is: £40.38. (excl. VAT)

The Kimya PC-S 3D filament is an amorphous thermoplastic. Polycarbonate (PC) is a transparent plastic. It offers high resistance to heat.

Please scroll down to see full product details 👇

Product details

The Kimya PC-S 3D filament is an amorphous thermoplastic. Polycarbonate (PC) is a transparent plastic. It offers high resistance to heat. It is solid and is suitable for demanding applications. It is well suited to a variety of applications such as the production of parts in the automotive, engineering and aerospace sectors, as well as for producing hulls, helmets, toys, electronic items, etc. The Kimya PC-S 3D filament has the following properties:

Can be sterilized
Resistant to heat (up to 140°C)
Food contact certification EU 10/2011, FDA 21 CFR
Complies with the REACH regulation and the RoHS directive

Store away from light, humidity and heat to maintain the properties of the product.

FILAMENT PROPERTIES

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0 mm
Density	ISO 1183-1	1.193 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@260°C – 5 kg)	25.5 g/10min

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION	XY
Printing Speed	45 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	295°C
Bed T°	105°C

PRINTED SPECIMENS PROPERTIES

	PROPERTIES	TEST METHODS	VALUES
THERMAL PROPERTIES	Maximum use T°	–	140 °C
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	2,172 MPa
	Tensile Strength	ISO 527-2/5A/50	53.8 MPa
	Tensile strain at strength	ISO 527-2/5A/50	3,7 %
	Tensile Stress at Break	ISO 527-2/5A/50	44.6 MPa
	Tensile strain at break (type A)	ISO 527-2/5A/50	4,8 %
	Flexural modulus	ISO 178	1,640 MPa
	Deformation at Flexural Strain	ISO 178	>5 %
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	67.7 MPa
	Charpy impact resistance	ISO 179-1/1eA	7.8 kJ/m²
	Shore Hardness	ISO 868	79,2D

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values – Properties can be influenced by production conditions.