Kimya PEI-9085 Black 1.75mm 500g

Sale

Original price was: £136.23.Current price is: £129.42. (excl. VAT)

The Kimya PEI-9085 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. If benefits from good resistance to temperature, high resistance to abrasion and high dimensional stability.

Please scroll down to see full product details 👇

Original price was: £136.23.Current price is: £129.42. (excl. VAT)

Product details

The Kimya PEI-9085 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. If benefits from good resistance to temperature, high resistance to abrasion and high dimensional stability. It is used in sectors such as aerospace, railway, electronics and transport etc. The Kimya PEI-9085 3D filament is based on ULTEM® by Sabic and has the following properties:

  • Temperature resistance
  • Flame retardant – eligible to UL94 V0
  • Railway fire and smoke standard EN45545
  • Aerospace FAR 25.853 Standard
  • Complies with the REACH regulation and the RoHS directive

Store away from light, humidity and heat to maintain the properties of the product.

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
Density ISO 1183-1 1.28 g/cm3
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min – 0-420°C) 178 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 25 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 360°C
Chamber T° 180°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
THERMAL PROPERTIES Heat distortion temperature (HDT) (0,45Mpa) ASTM D648 °C
Heat distortion temperature (HDT) (1,8Mpa) ASTM D648 158 °C
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/1A/50 2,322.5 MPa
Tensile Strength ISO 527-2/1A/50 69.7 MPa
Tensile strain at strength ISO 527-2/1A/50 6,2 %
Tensile Stress at Break ISO 527-2/1A/50 69.7 MPa
Tensile strain at break (type B et C) ISO 527-2/1A/50 6.2 %
Flexural modulus ISO 178 2,250 MPa
Deformation at Flexural Strain ISO 178 >5 %
Flexural stress at conventional deflection (3,5% strain)* ISO 178 74.5 MPa
Charpy impact resistance ISO 179/2C 11 kJ/m²
Shore Hardness ISO 868 78,7
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values – Properties can be influenced by production conditions.

PRINT SETTINGS:

  • PRINT SPEED : 20-35 mm/s
  • EXTRUSION TEMPERATURE : 350-380°C
  • PLATFORM TEMPERATURE : 120-160°C

MISCELLANEOUS

Spool Material PC
Steaming Temperature 120°C
Steaming Duration 4h-6h

Sale

Original price was: £136.23.Current price is: £129.42. (excl. VAT)

Need help? info@dream3d.co.uk / 02070888163

or

Buying in bulk or multiple items?

Kimya PEI-9085 Black 1.75mm 500g

0
Original price was: £136.23.Current price is: £129.42. (excl. VAT)

Ongoing Tech Support

Thousands of products available for next day delivery

We accept

You might also like

Loctite 3D 3843 HDT60 High Toughness – CLEAR 5KG

0
Original price was: £900.00.Current price is: £870.00. (excl. VAT)

Loctite 3D 3843 HDT60 High Toughness – CLEAR 1KG

0
Original price was: £175.00.Current price is: £165.00. (excl. VAT)

Loctite 3D 3172 High Impact – Clear 5KG

0
Original price was: £735.00.Current price is: £699.00. (excl. VAT)

Loctite 3D Cleaner T – 18KG

0
Original price was: £445.00.Current price is: £420.00. (excl. VAT)
Select the fields to be shown. Others will be hidden. Drag and drop to rearrange the order.
  • Image
  • SKU
  • Rating
  • Price
  • Stock
  • Availability
  • Add to cart
  • Description
  • Content
  • Weight
  • Dimensions
  • Additional information
Click outside to hide the comparison bar
Compare

Contact us for a quote