Sale

Kimya ABS-ESD Black 1.75mm 2.2kg

Sale

Original price was: £204.99.Current price is: £194.74. (excl. VAT)

The Kimya ABS-ESD 3D filament belongs to the styrenic polymer family.

Please scroll down to see full product details 👇

Original price was: £204.99.Current price is: £194.74. (excl. VAT)

Buy Now

Add to cart

Product details

ABS-ESD is an Acrylonitrile Butadiene Styrene to which an additive has been added to give it Electro Static Discharge properties: this material protects against electrostatic discharge. It also provides good impact resistance. It is a lightweight and rigid material that is also easy to print. It is ideal for applications requiring protection against electrostatic discharge. The Kimya ABS-ESD 3D filament has the following properties:

Easy to print
Protects against electrical discharge
Complies with the RoHS and REACH standards

Print Parameters and Specimens Dimensions

PRINTING DIRECTION	XY
Printing Speed	40 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	260°C
Bed T°	100°C

Filament Properties

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.03 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@220°C – 10 kg)	15 – 20 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-300°C)	107 °C

Printed Specimens Properties

	PROPERTIES	TEST METHODS	VALUES
ELECTRICAL PROPERTIES	Surface resistivity	ASTM D257	10⁷ – 10⁹ Ohms/m²
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	1,121 MPa
	Tensile Strength	ISO 527-2/5A/50	24.3 MPa
	Tensile strain at strength	ISO 527-2/5A/50	3.1 %
	Tensile Stress at Break	ISO 527-2/5A/50	19.8 MPa
	Tensile strain at break	ISO 527	6.4 %
	Flexural modulus	ISO 178	856 MPa
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	27.3 MPa
	Charpy impact resistance	ISO 179-1/1eA	10.9 kJ/m²
	Shore Hardness	ISO 868	66,7D

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values – Properties can be influenced by production conditions.