The Kimya ABS Kevlar 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene Kevlar (ABS Kevlar) is a composite filament enriched in aramid fibres.

Please scroll down to see full product details 👇

Original price was: £52.33.Current price is: £49.71. (excl. VAT)

Buy Now

Add to cart

Product details

Kimya Kevlar ABS offers properties that are superior to a standard ABS. It provides the printed parts with increased resistance to abrasion. It is used for finished parts and tools. The Kimya ABS Kevlar 3D filament has the following properties:

Low warpage – compared to ABS-S-
Lighter-weight printed parts – compared to ABS Carbon-
Complies with the REACH standard

Print Parameters and Specimens Dimensions

PRINTING DIRECTION	XY
Printing Speed	40-70 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	250-270°C
Bed T°	90-110°C

Filament Properties

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.036 g/cm3
Moisture rate	INS-6711	< 0.5 %
Melt flow index (MFI)	ISO 1133-1 (@220°C – 10 kg)	35 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-220°C)	100 °C

Printed Specimens Properties

PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	2,188 MPa
	Tensile Strength	ISO 527-2/5A/50	30 MPa
	Tensile strain at strength	ISO 527-2/1A/50	1.8 %
	Tensile Stress at Break	ISO 527-2/5A/50	27.3 MPa
	Tensile strain at break	ISO 527-2/5A/50	3.5 %
	Flexural modulus	ISO 178	1,662 MPa
	Flexural strength*	ISO 178	> 4,4 %
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	44.9 MPa
	Charpy impact resistance	ISO 179-1/1eA	5.1 kJ/m²
	Shore Hardness	ISO 868	70,1D

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values – Properties can be influenced by production conditions.