The Kimya HIPS-R 3D filament belongs to the styrenic polymer family. This High Impact PolyStyrene (HIPS) is a thermoplastic formulated from recycled materials and which“despite being recycled€“ boasts good resistance to impact and heat. It is highly impermeable, enabling it to be used in container applications free of any leakage. HIPS-R has another property distinguishing it from all other filaments: its solubility in D-limonene. Indeed, it can be used as a supporting material. It is used in the manufacture of packaging and also household appliances. The Kimya HIPS-R 3D filament has the following properties:

Good impact resistance
100% made from recycled materials
Soluble in D-Limonene
Complies with REACH and RoHS standards

FILAMENT PROPERTIES

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm
Density	ISO 1183-1	1.03 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@220°C“ 10 kg)	4.7 – 7.1 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min – 20-300°C)	97 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION	XY
Printing Speed	20-70 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	250-290°C
Bed T°	60-100°C

PRINTED SPECIMENS PROPERTIES

	PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES
	Tensile modulus	ISO 527-2/5A/50	1,273 MPa
	Tensile Strength	ISO 527-2/5A/50	23.7 MPa
	Tensile strain at strength	ISO 527-2/5A/50	1 %
	Tensile Stress at Break	ISO 527-2/5A/50	16.7 MPa
	Tensile strain at break	ISO 527-2/5A/50	11 %
	Flexural modulus	ISO 178	1,533 MPa
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	36.2 MPa
	Charpy impact resistance	ISO 179-1/1eA	7 kJ/m²
	Shore Hardness	ISO 868	76,6D