Kimya PA6-CO Black 1.75mm 750g

Sale

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior.

Please scroll down to see full product details 👇

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Product details

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior. Unlike other polyamide filaments on the market the PA6-CO is very easy to print and can be used seamlessly on open chamber 3D printers. It is the perfect standard polyamide go-to thanks to its inherent polyamide properties of high mechanical, chemical and  heat resistance. Due to the general moisture sensitivity of polyamides, the filament must be dried before printing.

  • Excellent printability even on open chamber printers
  • Low warping
  • Good wear resistance

2-years KIMYA warranty.
Store away from light, humidity and heat to maintain the properties of the product.

Filament Properties

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 2.85 ± 0.1 mm
Density ISO 1183-1 1.157 g/cm3
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min – 20-300°C) 65 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 0-300°C) 227 °C

Print Parameters and Specimens Dimensions

PRINTING DIRECTION XY
Printing Speed 55 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 270°C
Bed T° 75°C

Printed Specimens Properties

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,166 MPa
Tensile Strength ISO 527-2/5A/50 56.1 MPa
Tensile strain at strength ISO 527-2/5A/50 4.3 %
Tensile Stress at Break ISO 527-2/5A/50 13.4 MPa
Tensile strain at break (type A) ISO 527-2/5A/50 <14 %
Flexural modulus ISO 178 2,017 MPa
Deformation at Flexural Strain ISO 178 <5 %
Flexural stress at conventional deflection (3,5% strain)* ISO 178 65.9 MPa
Charpy impact resistance ISO 179-1/1eA 3.9 kJ/m²
Shore Hardness ISO 868 77,3

Once the spool is dried, we recommend that it be used within 24 hours and maximum 7 days without drying.

We have carried out several printing tests on Kimya PA6-CO and recommend the following:

Extrusion temperature: 260 – 290°C
Plate temperature: 75 – 100C
Printing speed: 40 – 70 mm/s

3D Printing Profiles

3D Printer Last update
Ultimaker S3 07/07/2022
Ultimaker S5 07/07/2022
PROPERTIES RATING
Ease to print 4/5
Rigidity 4/5
Impact Strength 2/5
Sensitivity to moisture 4/5
Temperature resistance 2/5
Weather Resistance 3/5
RoHs Compliant
EU 10/2011 Non Compliant
FDA Non Compliant
UL94 – V0 Non Compliant
ESD Protection Non Compliant

Sale

Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Need help? info@dream3d.co.uk / 02070888163

or

Buying in bulk or multiple items?

Kimya PA6-CO Black 1.75mm 750g

0
Original price was: £107.89.Current price is: £102.50. (excl. VAT)

Ongoing Tech Support

Thousands of products available for next day delivery

We accept

You might also like

Raise3D Pro3 Plus H2 Series

0
Original price was: £5,899.00.Current price is: £5,800.00. (excl. VAT)

Raise3D Pro3 H2 Series

0
Original price was: £4,549.00.Current price is: £4,500.00. (excl. VAT)
Select the fields to be shown. Others will be hidden. Drag and drop to rearrange the order.
  • Image
  • SKU
  • Rating
  • Price
  • Stock
  • Availability
  • Add to cart
  • Description
  • Content
  • Weight
  • Dimensions
  • Additional information
Click outside to hide the comparison bar
Compare

Contact us for a quote