The Kimya ABS Carbon 3D filament belongs to the styrenic polymer family. Acrylonitrile-butadiene-styrene-carbon (ABS Carbon) is a mixture of ABS and carbon fibres.
Please scroll down to see full product details 👇
£51.79Original price was: £51.79.£49.20Current price is: £49.20. (excl. VAT)
Product details
The carbon fibres give the filament improved rigidity compared to a standard ABS. This filament is highly valued by manufacturers of drones and by modelling aficionados. It is also used to make tools. The Kimya ABS Carbon 3D filament has the following properties:
No shrinkage
Better tensile modulus than ABS-S
Less warpage than ABS-S
Complies with the REACH standard
Print Parameters and Specimens Dimensions
PRINTING DIRECTION
XY
Printing Speed
50-60 mm/s
Infill
100% – rectilinear
Infill Angle
45°/-45°
Nozzle Temperature
245-270°C
Bed T°
90-95°C
Filament Properties
PROPERTIES
TEST METHODS
VALUES
Diameter
INS-6712
1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density
ISO 1183-1
1.045 g/cm3
Moisture rate
INS-6711
< 1 %
Melt flow index (MFI)
ISO 1133-1 (@220°C – 10 kg)
17.4 g/10min
Glass transition temperature (Tg)
ISO 11357-1 DSC (10°C/min – 20-220°C)
100 °C
Melting Temperature (Tm)
ISO 11357-1 DSC (10°C/min – 20-220°C)
30 °C
Printed Specimens Properties
PROPERTIES
TEST METHODS
VALUES
MECHANICAL PROPERTIES
Tensile modulus
ISO 527-2/5A/50
2,665 MPa
Tensile Strength
ISO 527-2/5A/50
35.7 MPa
Tensile Stress at Break
ISO 527-2/5A/50
37.5 MPa
Tensile strain at break
ISO 527
2 %
Flexural modulus
ISO 178
1,809 MPa
Flexural stress at conventional deflection (3,5% strain)*
ISO 178
51.4 MPa
Charpy impact resistance
ISO 179-1/1eA
6.2 kJ/m²
Shore Hardness
ISO 868
72.7
Note 1
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2
The data should be considered as indicative values – Properties can be influenced by production conditions.