Kimya PEKK-A Amber | 1.75mm | 500g


Original price was: £393.81.Current price is: £374.12. (excl. VAT)

The Kimya PEKK-A 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a thermoplastic polymer. PEKK-A is the amorphous form of PEKK, providing ease of printing.

Please scroll down to see full product details 👇

Original price was: £393.81.Current price is: £374.12. (excl. VAT)

Product details

This is a material that boasts good mechanical properties and is resistant to high temperatures (<150°C). Produced using KEPSTAN® Arkema, the Kimya PEKK-A 3D filament has been designed for technical applications. It can come into contact with hydrocarbons and fluids, enabling it to be used in multiple business sectors: aerospace, automotive, railways, etc. It has the following properties:

• Temperature resistance
• Flame retardant – eligible to UL94 V0
• Complies with the RoHS and REACH standard

Print Parameters and Specimens Dimensions

Printing Speed 20-40 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 350-400°C
Bed T° 110-170°C

Filament Properties

Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.261 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@380°C – 5 kg) 37 – 47 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min – 20-410°C) 159 °C
Heat distortion temperature (HDT) (1.8 MPa) ISO 75f 172°C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-410°C) 308 °C

Printed Specimens Properties

THERMAL PROPERTIES Maximum use T° 150 °C
Thermal conductivity ASTM E1530-11 0.21 W/mK
ELECTRICAL PROPERTIES Dielectric strength IEC 60243-1 (100µm) 84 KV/mm
Surface resistivity ASTM D257 1016 Ohms/m²
OUTGASSING Total Mass Loss (TML) ASTM E 595 0.27 %
Collected Volatile Condensable Material (CVCM) ASTM E 595 < 0.01 %
Water Vapor Recovered (WVR) ASTM E 595 0.29 %
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,510 MPa
Tensile Strength ISO 527-2/5A/50 65 MPa
Tensile strain at strength ISO 527-2/1A/50 5 %
Tensile Stress at Break ISO 527-2/5A/50 48 MPa
Tensile strain at break ISO 527-2/5A/50 >5 %
Flexural modulus ISO 178 1,660 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 63.2 MPa
Charpy impact resistance ISO 179-1/1eA 2.5 kJ/m²
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values – Properties can be influenced by production conditions.


Original price was: £393.81.Current price is: £374.12. (excl. VAT)

Need help? / 02070888163


Buying in bulk or multiple items?

Kimya PEKK-A Amber | 1.75mm | 500g

Original price was: £393.81.Current price is: £374.12. (excl. VAT)

Ongoing Tech Support

Thousands of products available for next day delivery

We accept

You might also like

Raise3D Pro3 Plus H2 Series

Original price was: £5,899.00.Current price is: £5,800.00. (excl. VAT)

Raise3D Pro3 H2 Series

Original price was: £4,549.00.Current price is: £4,500.00. (excl. VAT)
Select the fields to be shown. Others will be hidden. Drag and drop to rearrange the order.
  • Image
  • SKU
  • Rating
  • Price
  • Stock
  • Availability
  • Add to cart
  • Description
  • Content
  • Weight
  • Dimensions
  • Additional information
Click outside to hide the comparison bar

Contact us for a quote