Sale

Kimya PEBA-S Translucent | 2.85mm | 500g

Sale

Original price was: £47.94.Current price is: £45.54. (excl. VAT)

The Kimya PEBA-S 3D filament is a thermoplastic elastomer. Polyether block amide (PEBA) is produced via polycondensation of a carboxylic acid polyamide with an alcohol-terminated polyether.

Please scroll down to see full product details 👇

Original price was: £47.94.Current price is: £45.54. (excl. VAT)

Buy Now

Add to cart

Product details

PEBA is based on PEBAX by Arkema, is very flexible: it has the best elongation % in the range (>550%). It can be used to make shoe soles or other sports equipment (cycling, golf, American football helmet) as it offers substantial energy return. The Kimya PEBA-S 3D filament has the following properties:

Flexibility (>550% tensile elongation at break)
Impact resistance
Complies with theRoHS and REACH standards

Print Parameters and Specimens Dimensions

PRINTING DIRECTION	XY
Printing Speed	20-60 mm/s
Infill	100% – rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	210-260°C
Bed T°	70-90°C

Filament Properties

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.013 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@220°C – 10 kg)	13.6 g/10min
Melting Temperature (Tm)	ISO 11357-1 DSC (10°C/min – -90-190°C)	149 °C

Printed Specimens Properties

PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES	Tensile modulus	ISO 37/2/500	63 MPa
	Tensile Strength	ISO 37/2/500	32.8 MPa
	Tensile strain at strength	ISO 37/2/500	> 550 %
	Tensile Stress at Break	ISO 37/2/500	32.3 MPa
	Tensile strain at break	ISO 37/2/500	> 550 %
	Flexural modulus	ISO 178	70 MPa
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	2.4 MPa
	Charpy impact resistance	ISO 179-1/1eA	No Break
	Shore Hardness	ISO 868	93A

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values – Properties can be influenced by production conditions.